High resolution study of local stress inside alumina - micro mechanical analysis using laser scanning confocal microscope

The aim of this work is to measure the stress inside a hard micro object under extreme compression. To measure the internal stress, we compressed ruby spheres (a-Al2O3: Cr3+, 150 µm diameter) between two sapphire plates. Ruby fluorescence spectrum shifts to longer wavelengths under compression and can be related to the internal stress by a conversion coefficient. A confocal laser scanning microscope was used to excite and collect fluorescence at desired local spots inside the ruby sphere with spatial resolution of about 1 µm3. Under static external loads, the stress distribution within the center plane of the ruby sphere was measured directly for the first time. The result agreed to Hertz’s law. The stress across the contact area showed a hemispherical profile. The measured contact radius was in accord with the calculation by Hertz’s equation. Stress-load curves showed spike-like decrease after entering non-elastic phase, indicating the formation and coalescence of microcracks, which led to relaxing of stress. In the vicinity of the contact area luminescence spectra with multiple peaks were observed. This indicated the presence of domains of different stress, which were mechanically decoupled. Repeated loading cycles were applied to study the fatigue of ruby at the contact region. Progressive fatigue was observed when the load exceeded 1 N. As long as the load did not exceed 2 N stress-load curves were still continuous and could be described by Hertz’s law with a reduced Young’s modulus. Once the load exceeded 2 N, periodical spike-like decreases of the stress could be observed, implying a “memory effect” under repeated loading cycles. Vibration loading with higher frequencies was applied by a piezo. Redistributions of intensity on the fluorescence spectra were observed and it was attributed to the repopulation of the micro domains of different elasticity. Two stages of under vibration loading were suggested. In the first stage continuous damage carried on until certain limit, by which the second stage, e.g. breakage, followed in a discontinuous manner.

Measurement of the proton recoil spectrum in neutron beta decay with the spectrometer aSPECT : study of systematic effects

Precision measurements of observables in neutron beta decay address important open questions of particle physics and cosmology. In this thesis, a measurement of the proton recoil spectrum with the spectrometer aSPECT is described. From this spectrum the antineutrino-electron angular correlation coefficient a can be derived. In our first beam time at the FRM II in Munich, background instabilities prevented us from presenting a new value for a. In the latest beam time at the ILL in Grenoble, the background has been reduced sufficiently. As a result of the data analysis, we identified and fixed a problem in the detector electronics which caused a significant systematic error. The aim of the latest beam time was a new value for a with an error well below the present literature value of 4%. A statistical accuracy of about 1.4% was reached, but we could only set upper limits on the correction of the problem in the detector electronics, too high to determine a meaningful result. This thesis focused on the investigation of different systematic effects. With the knowledge of the systematics gained in this thesis, we are able to improve aSPECT to perform a 1% measurement of a in a further beam time.